Novilon Oilon

KAM6607

Novilon Oilon is a cast polyamide, which is inserted microscopic drops of oil during the production process. Regardless of the processing method, the oil content in the material mass causes the material to always be located on the sliding surface. The oil is evenly dispersed across the entire volume of the material in the form of microdrops.


Technical data

PROPERTY METHOD UNIT NOVILON OILON
PA 6 G+OIL
MECHANICAL      
* Tensile Strength ISO 527 MPa 69-71
* Flexural Strength ISO 178 MPa 131-133
* Compressive strength ISO 604 MPa 111-113
* Tensile E-Modulus ISO 527 MPa 3300-3650
*Flexural E - Modulus ISO 178 MPa 3150-3450
*Compressive -Modulus ISO 604 MPa 3300-4000
* Allowable compression during longer loading time - MPa 16
* Charpy Impact Strength -notched ISO 179   10,15
* Hardness (Shore D) ISO 868   67-80
* Coefficient of Friction ASTM D 1894   0,109
THERMAL      
 Melting temperature ISO 3146 °C 225
* Vicat Softening temperature ISO 306 °C 222
Operating temperature range  – (long term) - °C -40 do 110
Operating temperature – (short term) - °C 160
* Average Thermal Expansion (23 to 80°C) ASTM D 696 K-1 9,7·10-5
Thermal Conductivity ASTM C 177 W/mK 0,21
ELECTRICAL      
* * Dielectric Constant VDE 0303 Teil4
IEC 250
- 3,2
** Dielectric dissipation factor δ (at 1 MHz) VDE 0303 Teil4
IEC 250
- 0,011
 ** Surface resistivity VDE 0303 Teil3
IEC 93
Ω 2,2·1014
** Resistivity VDE 0303 Teil3
IEC 93
Ω cm 1,2·1016
Dielectric strength VDE 0303 Teil2
IEC 243
kV/mm 15-20
** Comparative Tracking Index VDE 0303 Teil1
IEC 112
- CTI 600M
OTHER      
Density ISO 1183 g/cm3 1,15
* Water Absorption (mass  change, 28 days, 65% RH,23°C) INTERNAL % 0,110
* Water Absorption (dimension change, 28 days,  65% RH, 23°C)   % 0,052
 Water Absorption from the air (long term on air 50% RH, 23°C) ASTM D 570 % 1,8-2
Water Absorption (Saturation) ASTM D 570 % 5-6
Specific properties Highly resistant to wear - low coefficient of friction – especially for bearings with high (p. v.) values    

* Tested by FACULTY OF MECHANICAL Engineering and naval architecture- Zagreb
** Tested by ISKRA KIBERNETIKA- Kranj

NOTES
All information contained in this literature corresponds with our current knowledge of the product.

In order to deliver a personalised, responsive service and to improve the site, we use cookies to remember and store information about how you use it. By using the website and agreeing to this policy, you consent to our use of cookies in accordance with the terms of this policy.

Accept Cookies Read more about Cookies